Near-frictionless diamond material created using nanotechnology
•
February 26, 2010
Mechanical engineers have fabricated an ultra sharp, diamond-like carbon tip possessing such high strength that it is 3,000 times more wear-resistant at the nanoscale than silicon. The end result is a diamond-like carbon material mass-produced at the nanoscale that doesn’t wear.
Comments
We're looking for comments that are interesting, substantial or highly amusing. If your comments are excessively self-promotional (use your real name, no keywords please), obnoxious, or even worse, boring, you will be banned from commenting. Your comment must be related to the post. Please do not comment on how great or wonderful the post is. All comments are moderated and, if approved, will display in less than 24 hours.